摘要： To investigate the corrosion products of Cr in molten FLiNaK salt (46.5 mol% LiF11.5 mol% NaF42 mol% KF), the corrosion test of the pure metal Cr was performed in molten FLiNaK salt at 700 ℃ for 200 h. The FLiNaK salt after the corrosion test was thoroughly investigated by X-ray absorption near-edge structure spectroscopy, a transmission electron microscope, and X-ray diffraction. The results demonstrate that the predominant oxidation state of Cr in FLiNaK salt is Cr3+, and the main corrosion product in cooled FLiNaK salt is K2NaCrF6.
分类： 核科学技术 >> 粒子加速器 提交时间： 2023-06-18 合作期刊: 《Nuclear Science and Techniques》
ZHANG Li-Li
YAN Shuai
JIANG Sheng
YANG Ke
WANG Hua
HE Shang-Ming
LIANG Dong-Xu
ZHANG Ling
HE Yan
LAN Xu-Ying
MAO Cheng-Wen
WANG Juan
JIANG Hui
ZHENG Yi
DONG Zhao-Hui
ZENG Le-Yong
Li Ai-Guo
摘要： The hard X-ray micro-focusing beamline (BL15U1) of SSRF is dedicated to hard X-ray micro/nano-spectrochemical analysis consisting of X-ray fluorescence (XRF), X-ray absorption spectroscopy (XAS) and X-ray diffraction (XRD) techniques. It is one of the most versatile instruments in hard X-ray microscopy science. Since its commission in 2009, BL15U1 has allocated over 25000 h beamtime for users, and about 700 proposals have been executed. The beamline and the experimental end-station were upgraded for several times to facilitate the users experimental needs and make it more convenient to operate. In this paper, we give a review on the beamline, describing its characteristics, recent technical developments, and a few examples of scientific progresses achieved in recent years on BL15U1.
分类： 核科学技术 >> 粒子加速器 提交时间： 2023-06-18 合作期刊: 《Nuclear Science and Techniques》
摘要： Microstructure and oxidation behavior of modified Ni-16Mo-7Cr-4Fe alloys by yttrium microalloying were investigated by scanning electron microscopy, transmission electron microscopy, grazing incident X-ray diffraction and synchrotron radiation X-ray fluorescence. M6C and Ni17Y2 phases were observed and the amount of Ni17Y2 increased with yttrium concentration. When the yttrium concentration increased to 0.43wt.%, some Ni17Y2 chains and multi phase regions containing Ni17Y2, M6C and phase appeared, which is harmful for the oxidation resistance. The alloy containing 0.05wt.% yttrium showed the best oxidation resistance, which derives its oxidation resistance from the adequate concentration of yttrium in the solid-solution ( phase), the formation of the protective layer of YCrO3 and chromia oxide and the strengthening effect of yttrium on oxide boundaries.
点击量
通过
点击量
下载量
评论