分类: 物理学 >> 交叉学科物理及相关领域的科学与技术 提交时间: 2018-03-30
摘要: AgSbTe2 bulk sample is obtained by hot-pressing under different fabrication parameters, and their thermoelectric properties are investigated in the temperature range of 300-550K. The highest ZT=0.86 is achieved at 475K for the sample hot-pressed at 423K and 500MPa due to the lower thermal conductivity and higher power factor. The results indicate that the optimized thermoelectric properties can be obtained for AgSbTe2 compound at the sintering temperature of 423K under the pressure of 500MPa.
分类: 物理学 >> 交叉学科物理及相关领域的科学与技术 提交时间: 2018-03-30
摘要: Gd-doped compounds CuGa1-xGdxTe2 (0x0.02) incorporated with tellurium nanoparticles are synthesized by fusion method. Their thermoelectric properties are investigated in the temperature range of 300-800K. The results indicate that the synergistic effect of Gd-doping and Te incorporation remarkably enhances the thermoelectric performance of CuGaTe2. Specially, the thermal conductivity of the specimen CuGa0.98Gd0.02Te2/0.7vol.%Te reduces to 0.45 Wm-1K-1 at 684K, which is ~74% smaller than that of pure CuGaTe2 (=1.76 Wm-1K-1 at 684K) due to the incorporation of nanostructure Te. The thermoelectric figure of merit value (ZT) reaches 0.75 at 737K for the specimen CuGa0.99Gd0.01Te2/0.7vol.%Te, which is ~115% larger than that of pure CuGaTe2.