Cu precipitates in hydrogen ion irradiated Fe-0.3%Cu alloy investigated by positron annihilation spectroscopy

分类： 物理学 >> 凝聚态:结构、力学和热性能 提交时间： 2017-03-26

Shuoxue Jin Xingzhong Cao Peng Zhang Eryang LU Liping Guo RuiSheng Yu Baoyi Wang

摘要： The formation of Cu precipitates in Fe-0.3%Cu binary model alloy after hydrogen ion irradiation at 400 was investigated by positron annihilation spectroscopy based on slow positron beam. In order to study the effect of elevated temperature for the Cu precipitates, the annealing treatment at 400 in Fe-0.3%Cu alloy was also investigated. The S-parameters of specimens increased with the irradiation dose increased, especially in the damage peak region. H+ implantation produced a large number of vacancy-type defects in Fe-0.3%Cu alloy. Compared to the unirradiated samples, the irradiated specimens show an overall major increase in W parameter values. Experimental results indicate that Cu precipitates formed easily under lower irradiation dose at elevated temperature. No obvious Cu precipitates formed when Fe-0.3%Cu alloy was annealed for 2h at 400 .

同行评议状态:待评议

 点击量 2213  下载量 1231  评论