摘要: The effect of annealing on VmHn complexes and Cu precipitate behaviors in hydrogen ion irradiated Fe and Fe-0.3%Cu alloys was investigated by positron annihilation spectroscopy using a slow positron beam. The results of S parameters indicated that the room temperature irradiation was benefit for the formation of the VmHn complex compared to the elevated temperature irradiation. The S-W results confirmed the formation of Cu precipitates in Fe-0.3%Cu even at the irradiation dose of 0.1 dpa. The formation of the evident S value peaks in the damage region after annealing treatment suggested that the VmHn complexes were broken and a larger of hydrogen atoms were escaping. The residual vacancy defects would migrate towards both the surface region and the opposite direction with the increasing annealing temperature.