摘要: Antireflection (AR) coatings that exhibit multi-
functional characteristics, including high transparency, robust
resistance to moisture, high hardness, and antifogging proper-
ties, were developed based on hollow silica−silica nano-
composites. These novel nanocomposite coatings with a
closed-pore structure, consisting of hollow silica nanospheres
(HSNs) infiltrated with an acid-catalyzed silica sol (ACSS),
were fabricated using a low-cost sol−gel dip-coating method. The refractive index of the nanocomposite coatings was tailored by controlling the amount of ACSS infiltrated into the HSNs during synthesis. Photovoltaic transmittance (TPV) values of 96.86− 97.34% were obtained over a broad range of wavelengths, from 300 to 1200 nm; these values were close to the theoretical limit for a lossy single-layered AR coating (97.72%). The nanocomposite coatings displayed a stable TPV, with degradation values of less than 4% and 0.1% after highly accelerated temperature and humidity stress tests, and abrasion tests, respectively. In addition, the nanocomposite coatings had a hardness of approximately 1.6 GPa, while the porous silica coatings with an open-pore structure showed more severe degradation and had a lower hardness. The void fraction and surface roughness of the nanocomposite coatings could be controlled, which gave rise to near-superhydrophilic and antifogging characteristics. The promising results obtained in this study suggest that the nanocomposite coatings have the potential to be of benefit for the design, fabrication, and development of multifunctional AR coatings with both omnidirectional broadband transmission and long-term durability that are required for demanding outdoor applications in energy harvesting and optical instrumentation in extreme climates or humid conditions.
-
期刊:
ACS APPLIED MATERIALS & INTERFACES
-
分类:
物理学
>>
普通物理:统计和量子力学,量子信息等
-
引用:
ChinaXiv:201705.00450
(或此版本
ChinaXiv:201705.00450V1)
DOI:10.12074/201705.00450V1
CSTR:32003.36.ChinaXiv.201705.00450.V1
- 推荐引用方式:
Zhang, XP [Zhang, Xianpeng][ 1 ],Lan, PJ [Lan, Pinjun][ 1 ],Lu, YH [Lu, Yuehui][ 1 ],Li, J [Li, Jia][ 1 ],Xu, H [Xu, Hua][ 2 ],Zhang, J [Zhang, Jing][ 1 ],Lee, Y [Lee, YoungPak][ 3,4 ],Rhee, JY [Rhee, Joo Yull][ 5 ],Choy, KL [Choy, Kwang-Leong][ 6 ],Song, WJ [Song, Weijie][ 1 ].(2017).Multifunctional Antireflection Coatings Based on Novel Hollow Silica-Silica Nanocomposites.中国科学院科技论文预发布平台.[ChinaXiv:201705.00450]
(点此复制)